effects of initial δ phase on hot tensile deformation behaviors and fracture characteristics of a typical ni-based superalloy

, , , , ,

materials science&engineeringa 598(2014)251–262,-0001,():

url:

摘要/描述

uniaxial tensile tests of a typical ni-based superalloy are conducted under the deformation temperature range of 920-1010 oc and strain rate range of 0.01-0.001 1/s. the effects of initial δ phase ( ) on the hot tensile deformation behaviors and fracture characteristics are discussed in detail. the results show that: (1) for the studied ni-based superalloy with a large amount of δ phase, the flow stress curves are composed of three distinct stages, i.e., work hardening stage, flow softening stage and the final fracture stage. (2) the initial δ phase has significant effects on the deformation behaviors of the studied superalloy. δ phase can cause the obvious work hardening at the beginning of hot deformation, and then accelerates the flow softening by promoting the dynamic recrystallization with further straining. with the increase of initial δ phase, the strain rate sensitivity coefficient decreases firstly and then increases. (3) the combined effects of localized necking and microvoid coalescence cause the final fracture of specimens. the increase of initial δ phase increases the density of nucleus for the formation of microvoids, and promotes the nucleation and coalescence of microvoids.

关键词:
  • 问答

    暂无问题,成为第一个提问者

【免责声明】以下全部内容由[蔺永诚]上传于[2014年02月03日 23时17分18秒],全讯担保网的版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。

我要评论

全部评论 0

本学者其他成果

同领域成果

网站地图